Exploring metal hydrides using autoclave and multi-anvil hydrogenations

152021-Thumbnail Image.png
Description
Metal hydride materials have been intensively studied for hydrogen storage applications. In addition to potential hydrogen economy applications, metal hydrides offer a wide variety of other interesting properties. For example, hydrogen-dominant materials, which are hydrides with the highest hydrogen content

Metal hydride materials have been intensively studied for hydrogen storage applications. In addition to potential hydrogen economy applications, metal hydrides offer a wide variety of other interesting properties. For example, hydrogen-dominant materials, which are hydrides with the highest hydrogen content for a particular metal/semimetal composition, are predicted to display high-temperature superconductivity. On the other side of the spectrum are hydrides with small amounts of hydrogen (0.1 - 1 at.%) that are investigated as viable magnetic, thermoelectric or semiconducting materials. Research of metal hydride materials is generally important to gain fundamental understanding of metal-hydrogen interactions in materials. Hydrogenation of Zintl phases, which are defined as compounds between an active metal (alkali, alkaline earth, rare earth) and a p-block metal/semimetal, were attempted by a hot sintering method utilizing an autoclave loaded with gaseous hydrogen (< 9 MPa). Hydride formation competes with oxidative decomposition of a Zintl phase. The oxidative decomposition, which leads to a mixture of binary active metal hydride and p-block element, was observed for investigated aluminum (Al) and gallium (Ga) containing Zintl phases. However, a new phase Li2Al was discovered when Zintl phase precursors were synthesized. Using the single crystal x-ray diffraction (SCXRD), the Li2Al was found to crystallize in an orthorhombic unit cell (Cmcm) with the lattice parameters a = 4.6404(8) Å, b = 9.719(2) Å, and c = 4.4764(8) Å. Increased demand for materials with improved properties necessitates the exploration of alternative synthesis methods. Conventional metal hydride synthesis methods, like ball-milling and autoclave technique, are not responding to the demands of finding new materials. A viable alternative synthesis method is the application of high pressure for the preparation of hydrogen-dominant materials. Extreme pressures in the gigapascal ranges can open access to new metal hydrides with novel structures and properties, because of the drastically increased chemical potential of hydrogen. Pressures up to 10 GPa can be easily achieved using the multi-anvil (MA) hydrogenations while maintaining sufficient sample volume for structure and property characterization. Gigapascal MA hydrogenations using ammonia borane (BH3NH3) as an internal hydrogen source were employed in the search for new hydrogen-dominant materials. Ammonia borane has high gravimetric volume of hydrogen, and additionally the thermally activated decomposition at high pressures lead to a complete hydrogen release at reasonably low temperature. These properties make ammonia borane a desired hydrogen source material. The missing member Li2PtH6 of the series of A2PtH6 compounds (A = Na to Cs) was accessed by employing MA technique. As the known heavier analogs, the Li2PtH6 also crystallizes in a cubic K2PtCl6-type structure with a cell edge length of 6.7681(3) Å. Further gigapascal hydrogenations afforded the compounds K2SiH6 and Rb2SiH6 which are isostructural to Li2PtH6. The cubic K2SiH6 and Rb2SiH6 are built from unique hypervalent SiH62- entities with the lattice parameters of 7.8425(9) and 8.1572(4) Å, respectively. Spectroscopic analysis of hexasilicides confirmed the presence of hypervalent bonding. The Si-H stretching frequencies at 1550 cm-1 appeared considerably decreased in comparison with a normal-valent (2e2c) Si-H stretching frequencies in SiH4 at around 2200 cm-1. However, the observed stretching modes in hypervalent hexasilicides were in a reasonable agreement with Ph3SiH2- (1520 cm-1) where the hydrogen has the axial (3e4c bonded) position in the trigoal bipyramidal environment.
Date Created
2013
Agent

First principles exploration of crystal structures and physical properties of silicon hydrides KSiH₃ and K₂SiH₆, alkali and alkaline earth metal carbides, and II-V semiconductors ZnSb and ZnAs

151955-Thumbnail Image.png
Description
This dissertation is focused on material property exploration and analysis using computational quantum mechanics methods. Theoretical calculations were performed on the recently discovered hexahydride materials A2SiH6 (A=Rb, K) to calculate the lattice dynamics of the systems in order to check

This dissertation is focused on material property exploration and analysis using computational quantum mechanics methods. Theoretical calculations were performed on the recently discovered hexahydride materials A2SiH6 (A=Rb, K) to calculate the lattice dynamics of the systems in order to check for structural stability, verify the experimental Raman and infrared spectrospcopy results, and obtain the theoretical free energies of formation. The electronic structure of the systems was calculated and the bonding and ionic properties of the systems were analyzed. The novel hexahydrides were compared to the important hydrogen storage material KSiH3. This showed that the hypervalent nature of the SiH62- ions reduced the Si-H bonding strength considerably. These hydrogen rich compounds could have promising energy applications as they link to alternative hydrogen fuel technology. The carbide systems Li-C (A=Li,Ca,Mg) were studied using \emph{ab initio} and evolutionary algorithms at high pressures. At ambient pressure Li2C2 and CaC2 are known to contain C22- dumbbell anions and CaC2 is polymorphic. At elevated pressure both CaC2 and Li2C2 display polymorphism. At ambient pressure the Mg-C system contains several experimentally known phases, however, all known phases are shown to be metastable with respect to the pure elements Mg and C. First principle investigation of the configurational space of these compounds via evolutionary algorithms results in a variety of metastable and unique structures. The binary compounds ZnSb and ZnAs are II-V electron-poor semiconductors with interesting thermoelectric properties. They contain rhomboid rings composed of Zn2Sb2 (Zn2As2) with multi-centered covalent bonds which are in turn covalently bonded to other rings via two-centered, two-electron bonds. Ionicity was explored via Bader charge analysis and it appears that the low ionicity that these materials display is a necessary condition of their multicentered bonding. Both compounds were found to have narrow, indirect band gaps with multi-valley valence and conduction bands; which are important characteristics for high thermopower in thermoelectric materials. Future work is needed to analyze the lattice properties of the II-V CdSb-type systems, especially in order to find the origin of the extremely low thermal conductivity that these systems display.
Date Created
2013
Agent

High pressure and high temperature study on lithium carbide (Li₂C₂) and calcium carbide (CaC₂): an attempt to make a novel polyanionic form of carbon

151208-Thumbnail Image.png
Description
Carbon lacks an extended polyanionic chemistry which appears restricted to carbides with C4-, C22-, and C34- moieties. The most common dimeric anion of carbon atoms is C22- with a triple bond between the two carbon atoms. Compounds containing the dicarbide

Carbon lacks an extended polyanionic chemistry which appears restricted to carbides with C4-, C22-, and C34- moieties. The most common dimeric anion of carbon atoms is C22- with a triple bond between the two carbon atoms. Compounds containing the dicarbide anion can be regarded as salts of acetylene C2H2 (ethyne) and hence are also called acetylides or ethynides. Inspired by the fact that molecular acetylene undergoes pressure induced polymerization to polyacetylene above 3.5 GPa, it is of particular interest to study the effect of pressure on the crystal structures of acetylides as well. In this work, pressure induced polymerization was attempted with two simple metal acetylides, Li2C2 and CaC2. Li2C2 and CaC2 have been synthesized by a direct reaction of the elements at 800ºC and 1200ºC, respectively. Initial high pressure investigations were performed inside Diamond anvil cell (DAC) at room temperature and in situ Raman spectroscopic measurement were carried out up to 30 GPa. Near 15 GPa, Li2C2 undergoes a transition into a high pressure acetylide phase and around 25 GPa this phase turns amorphous. CaC2 is polymorphic at ambient pressure. Monoclinic CaC2-II does not show stability at pressures above 1 GPa. Tetragonal CaC2-I is stable up to at least 12 GPa above which possibly a pressure-induced distortion occurs. At around 18 GPa, CaC2 turns amorphous. In a subsequent series of experiments both Li2C2 and CaC2 were compressed to 10 GPa in a multi anvil (MA) device and heated to temperatures between 300 and 1100oC for Li2C2, and 300°C to 900°C for CaC2. The recovered products were analyzed by PXRD and Raman spectroscopy. It has been observed that reactions at temperature higher than 900°C were very difficult to control and hitherto only short reaction times could be applied. For Li2C2, a new phase, free of starting material was found at 1100°C. Both the PXRD patterns and Raman spectra of products at 1100oC could not be matched to known forms of carbon or carbides. For CaC2 new reflections in PXRD were visible at 900ºC with the starting material phase.
Date Created
2012
Agent

Synthesis of mesoporous metal oxide materials

151141-Thumbnail Image.png
Description
Nanoporous crystalline oxides with high porosity and large surface areas are promising in catalysis, clean energy technologies and environmental applications all which require efficient chemical reactions at solid-solid, solid-liquid, and/or solid-gas interfaces. Achieving the balance between open porosity and structural

Nanoporous crystalline oxides with high porosity and large surface areas are promising in catalysis, clean energy technologies and environmental applications all which require efficient chemical reactions at solid-solid, solid-liquid, and/or solid-gas interfaces. Achieving the balance between open porosity and structural stability is an ongoing challenge when synthesizing such porous materials. Increasing porosity while maintaining an open porous network usually comes at the cost of fragility, as seen for example in ultra low density, highly random porous aerogels. It has become increasingly important to develop synthetic techniques that produce materials with these desired properties while utilizing low cost precursors and increasing their structural strength. Based on non-alkoxide sol-gel chemistry, two novel synthetic methods for nanoporous metal oxides have been developed. The first is a high temperature combustion method that utilizes biorenewable oil, affording gamma alumina (Al2O3) with a surface area over 300 cm3/g and porosity over 80% and controllable pore sizes (average pore width 8 to 20 nm). The calcined crystalline products exhibit an aerogel-like textural mesoporosity. To demonstrate the versatility of the new method, it was used to synthesize highly porous amorphous silica (SiO2) which exhibited increased mechanical robustness while achieving a surface area of 960 m2/g and porosity of 85%. The second method utilizes sequential gelation of inorganic and organic precursors forming an interpenetrating inorganic/organic gel network. The method affords yttria-stabilized zirconia with surface area over 90 cm3/g and porosity over 60% and controllable pore sizes (average pore width 6 to 12 nm). X-ray diffraction, gas sorption analysis, Raman spectroscopy, nuclear magnetic resonance spectroscopy and electron microscopy were all used to characterize the structure, morphology, and the chemical structure of the newly afforded materials. Both novel methods produce products that show superior pore properties and robustness compared to equivalent commercially available and currently reported materials.
Date Created
2012
Agent

Synthesis, structures and properties of thermoelectric materials in the Zn-Sb-In system

149883-Thumbnail Image.png
Description
The challenging search for clean, reliable and environmentally friendly energy sources has fueled increased research in thermoelectric materials, which are capable of recovering waste heat. Among the state-of-the-art thermoelectric materials β-Zn4Sb3 is outstanding because of its ultra-low glass-like thermal conductivity.

The challenging search for clean, reliable and environmentally friendly energy sources has fueled increased research in thermoelectric materials, which are capable of recovering waste heat. Among the state-of-the-art thermoelectric materials β-Zn4Sb3 is outstanding because of its ultra-low glass-like thermal conductivity. Attempts to explore ternary phases in the Zn-Sb-In system resulted in the discovery of the new intermetallic compounds, stable Zn5Sb4In2-δ (δ=0.15) and metastable Zn9Sb6In2. Millimeter-sized crystals were grown from molten metal fluxes, where indium metal was employed as a reactive flux medium.Zn5Sb4In2-δ and Zn9Sb6In2 crystallize in new structure types featuring complex framework and the presence of structural disorder (defects and split atomic positions). The structure and phase relations between ternary Zn5Sb4In2-δ, Zn9Sb6In2 and binary Zn4Sb3 are discussed. To establish and understand structure-property relationships, thermoelectric properties measurements were carried out. The measurements suggested that Zn5Sb4In2-δ and Zn9Sb6In2 are narrow band gap semiconductors, similar to β-Zn4Sb3. Also, the peculiar low thermal conductivity of Zn4Sb3 (1 W/mK) is preserved. In the investigated temperature range 10 to 350 K Zn5Sb4In2-δ displays higher thermoelectric figure of merits than Zn4Sb3, indicating a potential significance in thermoelectric applications. Finally, the glass-like thermal conductivities of binary and ternary antimonides with complex structures are compared and the mechanism behind their low thermal conductivities is briefly discussed.
Date Created
2011
Agent

Superconductivity of SrAlGe and BaAlGe: structure and dynamics of SrAlGeH and BaAlGeH

149545-Thumbnail Image.png
Description
The discovery of the superconductor MgB2 led to the increase of research activity for more compounds adopting the AlB2 structure type and containing superconductive properties. The prominent successor compounds were the silicide systems, AeAlSi (Ae=Sr, Ba, Ca). Presented here

The discovery of the superconductor MgB2 led to the increase of research activity for more compounds adopting the AlB2 structure type and containing superconductive properties. The prominent successor compounds were the silicide systems, AeAlSi (Ae=Sr, Ba, Ca). Presented here is an extension of this investigation to the germanides, SrAlGe and BaAlGe. The ternary structures were synthesized through arc-melting elemental stoichiometric mixtures and structurally characterized by x-ray powder diffraction. Both crystallize as the hexagonal SrPtSb structure type, a variant of the AlB2 structure type. The low temperature region was measured on a Vibrating Sample Magnetometer (VSM) and both present the onset of superconductivity below 7K. These compounds are susceptible to hydrogen absorption and the new polyanionic hydrides, SrAlGeH and BaAlGeH, structural and dynamic properties are presented. The hydrides were synthesized via two distinct methods. One method is the reaction of SrH2 (BaH2) with elemental mixture of the Al and Ge under pressurized hydrogen and the other is a hydrogenation of the SrAlGe and BaAlGe. Both crystallize in the trigonal SrAlSiH structure type, as determined from Rietveld analysis on powder neutron diffraction measurements. The hydrogen is coordinated by both the active metal and aluminum atoms, providing a unique environment for studying metal-hydrogen interactions. When exposed to air, both the hydrides and alloys transform from a crystalline grey to an amorphous yellow powder accompanied by a dramatic volume increase. Infrared spectroscopy shows the disappearance of the bands associated with the Al-H bond and the appearance of Ge-H and O-H bands. This indicates the material reacts with atmospheric water.
Date Created
2011
Agent