We demonstrate transverse-magnetic (TM) dominant deep-ultraviolet (DUV) stimulated emission from photo-pumped AlGaN multiple-quantum-well lasers grown pseudomorphically on an AlN/sapphire template by means of photoluminescence at room temperature. The TM-dominant stimulated emission was observed at wavelengths of 239, 242, and 243 nm with low thresholds of 280, 250, and 290 kW/cm[superscript 2], respectively. In particular, the lasing wavelength of 239 nm is shorter compared to other reports for AlGaN lasers grown on foreign substrates including sapphire and SiC. The peak wavelength difference between the transverse-electric (TE)-polarized emission and TM-polarized emission was approximately zero for the lasers in this study, indicating the crossover of crystal-field split-off hole and heavy-hole valence bands. The rapid variation of polarization between TE- and TM-dominance versus the change in lasing wavelength from 243 to 249 nm can be attributed to a dramatic change in the TE-to-TM gain coefficient ratio for the sapphire-based DUV lasers in the vicinity of TE-TM switch.

Optically pumped deep-ultraviolet (DUV) lasing with low threshold was demonstrated from AlGaN-based multiple-quantum-well (MQW) heterostructures grown on sapphire substrates. The epitaxial layers were grown pseudomorphically by metalorganic chemical vapor deposition on (0001) sapphire substrates. Stimulated emission was observed at wavelengths of 256 nm and 249 nm with thresholds of 61 kW/cm² and 95 kW/cm² at room temperature, respectively. The thresholds are comparable to the reported state-of-the-art AlGaN-based MQW DUV lasers grown on bulk AlN substrates emitting at 266 nm. These low thresholds are attributed to the optimization of active region and waveguide layer as well as the use of high-quality AlN/sapphire templates. The stimulated emission above threshold was dominated by transverse-electric polarization. This work demonstrates the potential candidacy of sapphire substrates for DUV diode lasers.