The Engineering of Charge Density Waves in Lanthanum Based Layered Tellurides Through Synthesis and Characterization

In the Rare-earth-Tri-telluride family, (RTe3s) [R=La, Ce, Nd, Sm, Gd, Tb, Dy, Er, Ho, Tm] the emergence of Charge Density Waves, (CDW) has been under investigation for a long time due to broadly tunable properties by either chemical substitution or pressure application. These quasi 2D Layered materials RTe3s undergo Fermi Surface Nesting leading to CDW instability. CDWs are electronic instabilities found in low-dimensional materials with highly anisotropic electronic structures. Since the CDW is predominantly driven by Fermi-surface (FS) nesting, it is especially sensitive to pressure-induced changes in the electronic structure. The FS of RTe3s is a function of p-orbitals of Tellurium atoms, which are arranged in two adjacent planes in the crystal structure. Although the FS and electronic structure possess a nearly four-fold symmetry, RTe3s form an incommensurate CDW.This dissertation is structured as follows: Chapter 1 includes basic ideas of Quantum materials, followed by an introduction to CDW and RTe3s. In Chapter 2, there are fundamentals of crystal growth by Chemical Vapor Transport, including various precursors, transport agent, temperature gradient, and rate of the reaction. After the growth, the crystals were confirmed for lattice vibrations by Raman, for composition by Energy Dispersive Spectroscopy; crystal structure and orientation were confirmed by X-ray Diffraction; magnetic ordering was established by Vibrating sample measurement. Detailed CDW study was done on various RTe3s by Raman spectroscopy. The basic mechanism and instrumentations used in these characterizations are explained in Chapter 3. Chapter 4 includes experimental data for crystal growth and results of these characterizations for Parent RTe3s. Chapter 5 includes fundamental insights on Cationic alloying of RTe3s, along with one alloy system’s crystal growth and characterization. This work tries to explain the behavior of CDW by a Temperature-dependent Raman study of RTe3s established the CDW transition temperature accompanied by Phonon softening; Angle-resolved Raman data confirming the nearly four-fold symmetry; thickness-dependent Raman spectroscopy resulting in the conclusion that as thickness decreases CDW transition temperature increases. Also, CDW transition is analyzed as a function of alloying.